Molybdenum Disulfide (MoS2) Coatings

Molybdenum Disulfide (MoS2) Application Process:

1. Cleaning: Parts are cleaned to remove all oil, grease & other substances. Cast parts are de-gassed.

2. Pretreatment: Abrasive blast surface with 180-220 grit aluminum oxide Phosphate IAW MIL-DTL-16232, type M, class 3 or type Z, class 3

3. Material Preperation: MoS2® is rolled at 30 rpm for 30 minutes to ensure the coating has been adequately mixed.

4. Application: The coating is sprayed onto the item either manually or on one our automated production lines.

5. Cure / Bake: Depending on the coating used the part is cured in an oven at a temperature from 300°F to 400°F.

6. Inspection: Parts are inspected to ensure proper application.

粘结性润滑剂是一种固体润滑剂分散于有机溶剂中的分散系。它在金属表面形成粘胶体干膜，这层膜有很好的耐腐蚀性能，且其工作温度范围很大（-70℃-+380℃）。固体润滑剂在极重的载荷下有极低的摩擦系数，这是普通润滑剂无法达到的。
二硫化钼减磨涂层 是道康宁公司粘胶体润滑剂的一种，这类产品的每一种都是专门为特种操作及苛刻工况设计的。
特点
1 高的承载能力
2 长效润滑
3 耐腐蚀性能优
4 耐油、溶剂及液压流体
5 膜层表面干燥，不会粘附灰尘
6 即使是没有预处理的表面也具有很好的粘附性
7 可用作十分薄的膜（3微米）
使用
二硫化钼减磨涂层 适用于以下场合：
1 高载，低速
2 滑动或振动
3 极温
4 微动腐蚀
5 严格防止基体被腐蚀
6 多灰